Self Compacting Concrete (SCC) Prepared By Ravi Kumar Contents Introduction Problems with conventional concrete Benefits of SCC Mix design principles Constituent materials Properties of fresh SCC Tests Application References
Introduction Fresh concrete that can flow around reinforcement and consolidate within formwork under its own weight that exhibits no defects due to segregation or bleeding. The guiding principle for this type of concrete is that the sedimentation velocity of a particle is inversely proportional to the viscosity of the floating medium in which the particle exists. Source: https://wwwbuildipedia.com Problems with Conventional Concrete
Requirement of skilled worker for compaction in conventional concrete Difficult to use mechanical compaction for Underwater concreting Cast in-situ pile foundation Columns with congested reinforcement
Benefits of SCC Faster construction Reduction in site manpower Safer working environment Improved aesthetics
Easier placing Improved durability Requirements for Self-compacting concrete Filling ability
Passing ability Segregation resistance Mix design principles The flowability and viscosity of the paste is adjusted by proportioning the cement and additives water to powder ratio and then by adding super plasticizers and VMA . The paste is the vehicle for the transport of the aggregate, therefore the volume of the paste must be greater than the void volume in the
aggregate. In order to control temperature rise and thermal shrinkage cracking as well as strength, the fine powder should be added to keep the cement content at an acceptable level. e.g. fly ash, mineral filler, silica fume etc. Contd. SCC should have Low coarse aggregate content
Increased paste content Low water powder ratio Increased super plasticizer dosage Viscosity modifying agents Flow Chart for achieving self
compactibility Reduction of water to binder ratio Limitation of coarse aggregate content & maximum size High segregation resistance of mortar & concrete Addition of
mineral admixture Usage of Super plasticizer & VMA High Deformability of mortar & concrete Self compactibility Typical mix proportion values Constituent Typical range by
volume(liter/m3) Powder 160-240 Water 150-210 Coarse aggregate 270-360 water to powder ratio 0.80-1.10
Fine aggregate 48-55% of total aggregate weight Materials Selection Limits on the amount of marginally unsuitable aggregate. Choice of HRWR Choice of VMA
Interaction & compatibility between cement, HRWR, VMA Aggregate It is observed from these studies that self-compactability is achievable at lower cement (or fines) content when rounded aggregates are used, as compared to angular aggregates. Rounded aggregates would provide a better flowability and less blocking potential for a given water-to-powder ratio, compared to angular and semi-rounded aggregates.
To eliminate the poor gradation problem in aggregates, filler materials are used. Chemical Admixtures HRWRA helps in achieving excellent flow at low water contents and VMA reduces bleeding and improves the stability of the concrete mixture. HRWRAs that work on the principle of steric hindrance require a lower dosage compared to those based on electrostatic repulsion.
Acrylic copolymers (AC) and polycarboxylate ethers (PCE) are effective at lower dosages compared to sulfonated condensates of melamine (SMF) or naphthalene (SNF) formaldehyde. Mineral Admixture Fly ash: It reduces free drying shrinkage and restrains the shrinkage cracking width. Silica fume: it gives good cohesion, improved resistance to segregation. Silica fume is also very effective in reducing or eliminating bleeding.
Mineral fillers: The particle size distribution shape and water absorption of mineral fillers may affect the water demand or sensitivity. CaCO3 based minerals fillers (<0.125mm size) are widely used and can give excellent rheological properties and performance. Fresh Properties of SCC Filling Ability Slump flow test, T50 cm slump flow test, V-Funnel test Passing ability
J-ring test, U-box, L-box Segregation potential Settlement column Test, Sieve stability test, Penetration test Slump Flow Test It is done to access the horizontal flow of concrete in the absence of obstruction. It gives good assessment of filling ability.
Slump cone of 300 mm height, 100 mm upper diameter and 200 mm bottom diameter. The diameter of spread should be lie between 650 mm to 800 mm. The higher the flow value, greater its ability to fill formwork . Contd. Source: http://www.hindawi.com/journals/je/2013/912983/fig5/
J-Ring Test It determines the passing ability of SCC. It consist of ring of reinforcement bars that will fit around the slump cone. Slump cone is fitted with concrete and lifted up as in slump cone test. The acceptable difference in height between inside and outside should
be between 0 and 10 mm. Contd. Source: http://www.joostdevree.nl/shtmls/j_ring_test.shtml Curing Top surface dry quickly because of the increased quantity of paste, the low water/fines ratio and the lack of bleed water at the surface. To avoid this Initial curing should therefore commence as soon as practicable after placing and finishing in order to minimize the risk of surface crusting and shrinkage cracks caused by early age moisture
evaporation. Complexities involved in SCC Higher paste volume results in greater shrinkage and creep. Higher strength achievement leads to reduces the workability to unacceptable level Lateral Formwork pressure
Limit of flow distance of the concrete Application Two anchorages of Akashi-Kaikyo (Straits) Bridge, Japan. The volume of the cast concrete in the two anchorages amounted to 290,000 m3 The highest use of SCC in India was done at Delhi metro project. About 10000 m3 of SCC has been Used. At Kaiga nuclear power plant, SCC of Characteristic strength 30 MPa was
used. Contd. The Burj Khalifa is the tallest building in the world. SCC was used throughout the building and was pumped 166 stories above the ground. The Trump Tower in Chicago, Illinois was a major user of SCC. It is a 92story reinforced concrete project that required 3500 m3of SCC to be cast-in-place continuously for 22 hours to construct the mat foundation that supports the finished structure. The mix had a 7-day compressive strength of 68 MPa and a 28-day strength of 82 MPa . This single pour is the largest ever recorded to date in North America using SCC
Conclusion We can reduce the in-place cost and maker a safer working environment for the workers. SCC can be effectively placed in most congested areas and also where normal methods of vibration are not possible. Further research are required to interpret influence on the hardened properties of SCC more precisely.
The cost of SCC is 10-15 % higher than the conventional concrete. References 1. Okamura et al. Self-compacting concrete, Journal of Advanced Concrete Technology, vol. 1, no. 1, pp. 515,2003 2. SK Singh Self Compacting Concrete - A Paradigm Shift, Journal of New Building Materials & Construction World, Vol. 15, No. 3, pp 164180,September , 2009. 3. The European Guidelines for Self Compacting Concrete, May 2005 4. Eric P. Koehler et al. Aggregate in Self Consolidating Concrete, ICAR Project 108, March 2007 5. KHALEEL, O.R. et al. The Effect of Coarse Aggregate on Fresh and Hardened Properties of Self-Compacting Concrete (SCC), Elsevier, pp 805-813, 2011 Contd. 1. Filho et al. Hardened properties of self-compacting concrete A
statistical approach, Elsevier, Construction and Building Materials, pp 1608-1615, 2010 2. Schindler, K Anton et al. Properties of self-consolidating concrete for precast members, ACI Materials Journal, V. 104, No. 1, 2007 3. Specification and Guidelines for Self-Compacting Concrete, EFNARC, 2002 4. Ouchi et al. APPLICATIONS OF SELF-COMPACTING CONCRETE IN JAPAN, EUROPE AND THE UNITED STATES, ISHPC, 2003 5. R. Loser, A. Leemann, Shrinkage and restrained shrinkage cracking of self-compacting concrete compared to conventionally vibrated concrete, Materials and Structures, 2008
LMX theory suggests that early on in the relationship between a leader and a. given follower, a leader will implicitly categorize a follower as an "in" or as an "out." That relationship tends to remain fairly stable over time. Leaders...
Percent of Total Burden of Infectious Disease passes through Corrections Total HIV/AIDS 15% Chronic Hepatitis B 12-16% Hepatitis C 29-32% TB Disease 38% Hammett et al AJPH 2002 and 2009 Prevalence of Various Conditions Compared to General US Population Community...
PARA VI What is a good synonym for update, follow? ... COMMERCE COMMERCIAL UNCOMMERCIAL REVOLUTION REVOLUTIONARY REVOLUTIONISE REPUTE REPUTATION REPUTED REPUTABLE DISREPUTABLE COMFORT DISCOMFORT COMFORTABLE UNCOMFORTABLE RETAIL RETAILING RETAILER * Breaking into a new market (p. ...
N = 271 Chaplaincy: A Research-Informed Profession Reviews of Chaplaincy Research Mowat, Harriet (2008). The potential for efficacy of healthcare chaplaincy and spiritual care provision in the NHS (UK): A scoping review of recent research.
Spend this lesson drawing your second initial design idea for a thermometer screen. Label the materials and features of the design. ... Insert a 430mm M5 threaded rod into one of the holes in item1 Secure in place with an...
*Judith McFarlane, Jacquelyn C. Campbell, and Kathy Wilson, 2001, "The use of the justice system prior to intimate partner femicide, Criminal Justice Review, 26, 2, Autumn 2001, 193-208. ... Photo by Tony Webster. Intimate partner homicide (IPH) comprises the staple...
Ready to download the document? Go ahead and hit continue!